Epoxigraph 560 Plus

It is made from low-viscosity epoxy resins to facilitate the impregnation of glass and carbon fibres, providing excellent adhesion.

Technical information

  • High adhesive strength. 
  • Great chemical and mechanical resistance. 
  • Does not shrink when curing. 
  • High performance. 
  • Does not crystallise at low temperatures.
  • The application can be manual or by machine.
  • It must be ensured that the mixture is homogeneous before starting to apply the product.
  • Temperature affects drying time, with the product being designed for a working temperature between +30ºC and +50ºC. The higher the temperature, the shorter the life of the mixture.
  • Hardened product residues can only be removed mechanically.
  • The product should be stored in a dry place at a temperature not exceeding 25°C. 
  • Its expiration date is 1 year under these conditions. 
  • The available packaging is 1000 kg. 
  • For other quantities, please consult us.
  • Viscosity: 1000 – 1200 cp 
  • Density: 1.45 – 1.48 kg/l 
  • Mixing ratio: 100:15.4
  • Flexural modulus: 5064.8 MPa 
  • Flexural strength: 48.88 MPa 
  • Maximum flexion dL: 1 mm 
  • Tensile modulus: 4240 MPa 
  • Tensile strength: 29.7 MPa 
  • Elongation at break: 0.70%