EPOXIGRAPH 560 PLUS

Pultrusión con grafeno

EPOXIGRAPH 560 PLUS

It is manufactured from low viscosity epoxy resins to favour impregnation of glass and carbon fibers, providing high adhesion.

PROPERTIES

  • High adhesive strength.
  • High chemical and mechanical resistance.
  • No shrinkage on hardening.
  • High yield.
  • No crystallisation at low temperatures.

APPLICATIONS

  • Application can be manual or machine-applied.
  • The mixture must be ensured to be homogeneous, before starting to apply the product.
  • Temperature affects drying time, being designed for a working temperature between +30ºC and +50ºC.
  • The higher the temperature, the shorter the pot life of the mixture.
  • Any hardened product residues may only be removed by mechanic.

STORAGE AND PACKAGING

  • The product should be stored in a dry place at a temperature not exceeding 25ºC.
  • The expiry date is 1 year under these conditions.
  • The existing containers are 1000 kg.
  • For other quantities: contact us.

EPOXIGRAPH 560 PLUS CHARACTERISTICS

  • Viscosity: 1000 – 1200 cp
  • Density: 1.45 – 1.48 kg/l
  • Gel time: –
  • Drying 45º: –
  • Curing: –
  • Mix ratio: 100:15,4

EPOXIGRAPH HARDENER CHARACTERISTICS

  • Viscosity: 60 – 100 cp
  • Density: 1.00 – 1.04 kg/l
  • Gel time: –
  • Drying 45º: –
  • Curing: –
  • Mix ratio: 100:15,4

MIXTURE CHARACTERISTICS

  • Viscosity: 950 – 1050 cp
  • Density: 1.41 kg/l
  • Gel time: 20 – 25 min
  • Drying 45º: 40 – 50 min
  • Curing: 24 horas
  • Mix ratio: 100:15,4

MECHANICAL TESTING

  • Flexural modulus: 5064,8 MPa
  • Flexural strength: 48,88 MPa
  • Maximun deflection: 1 mm
  • Tensile modulus: 4240 MPa
  • Tensile strength: 29,7 MPa
  • Elongation at break: 0,70 %

  • tubo composmart
  • viga grafeno graphenano