REINFORGRAPH 901 PLUS PREMIUM

Pultrusión con grafeno

REINFORGRAPH 901 PLUS PREMIUM

Bisphenol A type epoxy vinilester resin with graphene and other loads, of high viscosity and low reactivity. It provides excellent corrosion resistance to a broad range of organic and inorganic acids, alkalis, oxidizing chemicals, and salt solutions, etc. It also provides very good mechanical strength such as tensile and flexural while incorporated as reinforcement onto the ceramic pieces, it can increase the maximum strength of the final pieces with very good adhesion.

PROPERTIES

  • High mechanical properties.
  • High chemical resistance.
  • Excellent corrosion resistance.
  • Very good adhesion and High maximum strength in ceramic pieces.

APPLICATIONS

  • It is specially designed as resin reinforcement for ceramic.
  • It has good adhesion and very low linear and volumetric shrinkage.
  • The percentage of mek peroxide to be added is between 1% and 1.2%, although it can be increased to 2% to reduce the gel time.
  • The application can be manual or by machine.
  • Can be used in ceramic industry.

STORAGE AND PACKAGING

  • The product should be stored in a dry place at a temperature not exceeding 25ºC.
  • The expiry date is 4 months under these conditions.
  • The existing containers are jerrycans, berrels, IBC.
  • For other quantities: contact us.

TECHNICAL CHARACTERISTICS

  • Appearance: Dark liquid
  • Specific Gravity: 1.8 – 2.0
  • Gel time (25ºC) (100/0.3 CO/0.6 PMEK): 40 – 45 min
  • Viscosity brookfield (SPL3V21 , 25ºC): 1200 – 1300 cps

MECHANICAL CHARACTERISTICS

  • Flexural modulus: 14938,66 MPa
  • Flexural strength: 40,87 MPa
  • Maximum deflection dL: 0,29 mm
  • Tensile modulus: 9250 MPa
  • Tensile strength: 29,5 MPa
  • Elongation ar break: 0,31 %

Mechanical properties of the catalysed resin

MECHANICAL CHARACTERISTICS IN CERAMIC REINFORCEMENT

  • Ceramic Sample Reference (100×17 mm): Thickness 3,4 mm; Maximum Strength 101 N; Mass 13,3 g
  • Ceramic Sample + Reinforgraph resin (0.5 mm): Thickness 3,9 mm; Maximum Strength 112 N; Mass 15,3 g
  • Ceramic Sample + Reinforgraph resin (1.1 mm): Thickness 4,5 mm; Maximum Strength 134 N; Mass 17,9 g